Dry cement-minral mixes
CONCRETE MIXES AND COMPOSITIONS
- Mix for hardening and rising adhesion of repair composition.
- Composition for corrosion-inhibiting and adhesion coating of steel reinforcement.
- Compositions of cement mortar and concrete:
- Water resistance;
- With high kinetics of hardening;
- non-shrinking and with regulate widening;
- with specified adhesion based on colloidal cement glues;
- resistance to corrosive medium;
- compositions for dry and wet gunning;
- high hard to 80 MPascal;
- compositions for injections into difficult for access places with making impervious beds.
All mixes are packed in moisture-resistant bags on 50 kg and ready to use after addition to mixing water.
| Tsemins TST |
|
| Tsemins TST (t) |
Mix for gunned concrete |
| Tsemins TST (w) |
Mix for water resistance concrete |
| Tsemins TST (p) |
Mix for concrete with regulate widening |
| Tsemins TST (k) |
Mix with high adhesion |
| Tsemins TST (a) |
Mix for concrete with resistance to corrosive medium
|
| |
|
| Tsemins TSI |
Mix for injection in interstice for prevention from water and other liquids filtration |
| Tsemins TSE |
Mix for repairing concrete coatings including roads, landing strip at normal and emergency conditions |
| Tsemins TSÀ |
Mix in constructional packing (chuck) for dead-ending of machine-tools park, attached implements, bushes and other kinds of hardware |
| |
|
Type of mix |
| Characteristics |
Tsemins TST |
Tsemins TSI |
Tsemins TSE |
Tsemins TSA |
|
| Bulk weight, kg/m3 |
1400-1800 |
1300-1500 |
1800-2100 |
1100-1200 |
| Aggregate size of mineral aggregate, no more than, mm |
10,0 |
2,0 |
10,0 |
— |
| Mobility |
slump, cm |
2-10 |
— |
1-4 |
— |
| flow, mm |
— |
180-200 |
— |
— |
| Water-solid relation, relative unit. |
0,11-0,18 |
0,30-0,35 |
0,12-0,14 |
0,25-0,30 |
| Time of setting |
begin, min. |
90-180 |
220-260 |
7-12 |
4-6 |
| end, min. |
240-360 |
400-450 |
15-18 |
10-12 |
| Compression strength , no less than, MPascal |
4 hours |
— |
— |
16-20 |
— |
| 1 day |
15-19 |
8-12 |
— |
40-50 |
| 2 days |
25-30 |
— |
— |
— |
| 3 days |
— |
22-30 |
— |
— |
| 7 days |
— |
— |
46-50 |
— |
| 28 days |
40-60 |
40-50 |
55-60 |
100-110 |
| Adhesion to concrete, no less than, MPascal |
1 day |
0,5 |
0,25 |
0,25 |
— |
| 28 days |
1,5 |
1,0 |
2,0 |
— |
| Freeze-thaw durability, no less cycles |
300 |
— |
350 |
— |
| Corrosion resistance factor (5 % solution Na2SO4) |
1,01 |
1,01 |
1,02 |
1,02 |
| Water resistance, MPascal |
0,8 - 1 |
0,8 |
0,8-1 |
— |
| Dilatation, % |
0-1 |
non-shrink |
non-shrink |
1,0 1 day |
| Time of retention of technological mobility, no less than, min |
90-120 |
100-150 |
10-15 |
— |
| Abradability, g/cm², no more |
— |
— |
0,2-0,3 |
— |
| Pulling effort, t |
— |
— |
— |
14-18 |
|
|